高分子材料加工工程专业外语考试资料

第一篇：高分子材料加工工程专业外语考试资料

1.Material

• polyethylene 聚乙烯,polypropylene 聚丙烯,polyamide(聚酰胺)尼龙,polyester 聚酯

• polystyrene 聚丙烯,polycarbonate 聚碳酸酯,polyvinyl chloride 聚氯乙烯,polymethyl methacrylate（PMMA）有机玻璃聚甲基丙烯酸甲酯

• synthesis 合成,polymerization 聚合,catalyst 催化剂,chemical reactivity 化学反应性,monomer 单体单体结构

• thermoplastic 热塑性塑料,thermoset热固性塑料,elastomer 弹性体

2.Structure

• double bond 双键,repeat unit 重复单元,conformation 构象, configuration构型pendant group 侧基,branch chain 支链,coil 线团

• number average molecular weight 数均分子量

• intermolecular attraction 分子间的吸引力,hydrogen bonding 氢键,entanglement 纠缠、纠结,orientation 取向• amorphous 非晶,crystalline 晶区,crosslinked交联的• nucleation 成核,folded chain model 折叠连模型,sphereulite 球晶• blend 混合,composite 复合,morphology 形态 ,Composition 组成,component组分,matrix phase聚集相• Infrared spectroscopy 红外吸收光谱法

• differential scanning calorimetry 差示扫描量热法

• X-ray diffraction X射线衍射

3.Property

• glass transition temperature 玻璃化转变温度,melting point 熔点,decomposition 分解,degradation 降解,thermal stability热稳定性 ,coefficient of thermal expansion 热膨胀系数 • impact toughness 冲击韧性,tensile strength 抗张强度,reinforcement 强化,melt index 熔融指数

• modulus 模数,stress-strain curve 应力-应变曲线,elongation at break 断裂伸长率,deformation 变形

• creep 蠕变,stress relaxation 应力松弛,annealing 退火 • shear-thinning / thickening 剪切稀释/增稠

• pseudoplastic 假塑性体,viscoelasticity 粘弹性

4.Processing

• twin-screw extruders 双螺杆挤出机

• injection molding 注塑

• die 冲模,mold 模,cavity 型腔• processing aids / additives 加工助剂,filler 填料 • melt,熔融plasticizing 塑化,solidify 固化

• Because of the close connection between the terms resins, plastics, and polymers, they are sometimes used interchangeably, although correctly used there are differences.To summarize, polymers are any material made up of molecular chains;plastics are synthetic, long-chain polymers that can be or have been shaped;and resins are solids or liquids that are subsequently shaped into a plastic part.因为树脂、塑料、和聚合物这些术语之间密切的联系,它们有时可以互换使用,虽然准确地使用有差异。总之,聚合物是由分子链构成的物质,塑料是合成的,长链的可以成形的聚合物,而树脂是以后可以形成一个塑料零件的固体或液体高聚物。

• The complexity in polymers arises because solid polymeric materials can exist, in two very distinct types of structure.In one type, the polymermoleculesarerandomlycoiledabouteachotherwith entanglement.This structure type is called amorphous.In the second type, the polymer molecules can pack together into regular, repeating structural patterns.These regularly packed regions are called crystals or crystalline regions.在聚合物的复杂性的产生是因为固体聚合物材料可以存在于两个非常不同的类型的结构中。在一个类型的结构中,聚合物分子随机盘绕互相纠缠，这种结构类型被称为非晶。在第二个类型的结构中、聚合物分子可以折叠成常规,重复的结构模式，这些结构区域经常被称为晶体或晶区。

• The most important(but not the only)feature of a polymer that determines whether it will be amorphous or crystalline is the shape of the polymer repeat unit.If the repeat unit is complex, especially with large pendant groups, the polymer cannot pack tightly together and will be amorphous.Some of the most common amorphous polymersarepolystyrene,acrylic,polycarbonate,andmost copolymers.•最重要的(但不是唯一的)决定一种聚合物是否是非晶态或晶态的一个重要特征是聚合物重复单位的形状。如果重复单位是复杂的,尤其是有大侧基,聚合物不能紧紧的折叠在一起,即是非晶态。一些最常见的非晶态高分子聚合物有聚苯乙烯、丙烯、聚碳酸酯和大多数共聚物。

• In addition to these structural factors, the crystallinity of polymers also depends upon molding or processing conditions.Crystallization in polymers takes time to occur.Therefore, factors such as cooling rate can have strong influences on the amount of the material that crystallizes, since below certain temperatures there is not sufficient molecular motion to allow the molecules to rearrange into a close packing configuration.除了这些结构性的本质因素之外，聚合物的结晶度还取决于成型或加工条件。聚合物的结晶需要时间。因此,冷却速率等因素可以对材料的结晶度产生很大影响影响,因为在一定的温度以下分子运动将减小到不足以使分子链重新排列一个紧密的折叠晶体构型。

• Most polymer materials have some characteristics that are similar to viscous liquids and some that are similar to elastic solids.These materialsarethereforeknownasviscoelastic.Viscoelastic materialscanbeeitherliquidorsolid,althoughthedistinction between liquids and solids in these materials is not a clear one.Thetimedependenceofviscoelasticmaterialsisanimportant consideration that significantly affects their behavior.Most polymer viscoelastic liquids exhibit shear-thinning, and many are thixotropic.大多数聚合物材料有一些特征,既类似于粘性液体又跟弹性固体相似。因此这些材料的这种性质被称为粘弹性。粘弹性材料可以是液体或固体,尽管液体和固体的区别在这些材料中并不明确。这些粘弹性材料的时间依赖性的是一个重要的考虑因素,很大程度上影响材料的性质。大多数聚合物粘弹性液体表现剪切稀释特性,而且许多是触变。

• The viscous nature of a polymer solid can be associated with long-range movements.The viscous material will move more freely than an elastic solid when a force is imposed, and all the energy input intothematerialmaynotbereturnedbecauseofpermanent deformations or the creation of internal heating.The long-range movements require moreenergyto activate than do the short-range movements.Hence, above a certain level of internal energy, the behavior of the material will more likely be dominated by long-range movements, and below this characteristic energy level, the material will exhibit only short-range movements.聚合物固体的粘性与协同运动有关。当施加力的时候粘性材料将比弹性固体材料运动的更加自由,所有输入材料的能量将不能返回来全部被吸收，用于使粘性材料产生永久变形或产生内能的增加。协同运动比短程运

动需要更多的能量来激发。因此,超过一定水平的内部能量，材料的行为将更倾向于分子链的协同动作,低于这一特定能级,材料会只展出分子内琏段的短程运动。

• The molecular interpretation of elastic and plastic behavior is that in the elastic region the strain results from recoverable movement-stretching out of the twisted molecules in the amorphous regions and minor deformations in the crystalline regions.At the yield point, nonrecoverablemovementsbeginthatresultinpermanent deformation.Some of the most common are disentanglement of the molecules, slip of one molecule past another in a way that the slipcouldnotberecovered,slipalongacrystalplane,and formation of a crack.弹性和塑性行为的分子水平的解释就是，在弹性区，应变来自于在非晶区和小变形的结晶区的分子的可恢复的伸展和扭曲。在屈服点,不可恢复的运动开始,导致永久变形。最常见有分子解缠,不可恢复的分子间滑动，沿晶面滑移,形成一个裂缝。

• High molecular weight favors high toughness.This results from the combination of higher strength and better sharing of the impact force along the polymer chain by causing more atoms to rotate, vibrate,andstretchtoabsorbtheenergyoftheimpact.Crystallinity gives higher strength but lower toughness unless the nature of the backbone changes.Crosslinking of a brittle polymer willusuallydecreasetoughnessbecauseoftheincreased limitationofmotionwithinthepolymermasscausedbythe intermolecular bonds.高分子量与高韧性城正比。这个是由高强度的分子间结合，和通过沿着聚合物链引起更多的原子旋转,震动,并延伸来吸收能量吸收冲击的能量，以更好的分担冲击力导致的。结晶度可以导致高强度同时降低韧性，除非分子链的主链改变。脆性聚合物的交联通常会降低韧性，因为分子间键会增加聚合物运动的限制。

• The differences between the commodity thermoplastics arise from the differences caused by the substitution of one functional group(atom)onthecarbon-carbondoublebond.Oneofthemost important effects is steric, that is, the consequences of differences in the size of the functional groups.When the functional groups are small(suchashydrogen),littlesterichindrance(interference becauseofsize)isencountered.Withoutsterichindrancethe polymers are relatively free to rotate, bend, and pack together.不同商品热塑性塑料之间的差异是由碳碳双键上的取代基官能团(原子)导致的。其中最重要的影响是空间,即不同取代基大小的差异导致。当官能团很小(比如氢),遭到的是小位阻(干扰因为大小)。如果没有位阻，聚合物会相对自由旋转,弯曲,并且混合在一起。

• Themajorityofengineeringthermoplasticsaresimilarinmany respects.Theyaregenerallystrongandhave,ahighuse temperature, good impact strength, good dimensional stability over awiderangeoftemperatures,generallygoodresistanceto environmental conditions, and are much more moldable than the metal,ceramic,orwoodpartsthattheyoftenreplace.Most engineering resins can also be made into fibers, films, and coatings, which is beyond the capability of most metals.大部分的工程热塑性塑料在许多方面是相似的。他们通常具有高的强度,使用温度,良好的冲击强度、在很宽的温度范围内良好的尺寸稳定性,较好的耐环境条件的性质,比它们所经常替代的金属、陶瓷、或木制品可塑性好得多。大多数工程树脂也可以被制成纤维,胶片,和涂料,这超出了大部分金属的性能。

• In addition to the shaping of parts, extrusion is the most efficient and widely used method for melting plastic resin as part of the process of adding or mixing fillers, colorants, and other additives into the molten plastic.Extrusion can be used to shape the part directly after this mixing or an extruder can be used as the melting device that is coupled with other shaping processes.When used for direct shaping, a shaping device or tool is placed directly on the end of the extrusion machine(extruder)and the process is called extrusion molding.除了铸塑零件以外,挤出成型是最有效的和广泛使用的把塑料树脂制成零件的方法,在融化过程要中添加或混合填料、着色剂、和其它添加剂到熔融塑料。挤出成型可以在混合后直接成型零件，或挤出机可以用作熔化装置,再加上其他成形过程。当用于直接成型,成形设备或工具是直接放在挤出机最后面的,这个过程叫做挤压成型。

• In normal plastics extrusion, plastics granules or pellets and any othermaterialstobemixed

withthemarefedintoahopper attached to the extrusion machine.From the hopper the material falls through feed throat onto the extrusion screw.This screw, which turns inside the extruder barrel, conveys the plastic forward into a heated region where the combination of external heating and heating from friction melts the plastic.The screw moves the molten plastic forward until it exits through a hole in the end of the extruder barrel.在正常的塑料挤出成型中，塑料颗粒或球和其他材料混合着被送入一个附加到挤压机上的漏斗中。通过漏斗材料从下料口落入挤出螺杆。这个螺杆在挤出机管道内旋转,将塑料向前传送到加热区，在这个区域外部加热和摩擦生热结合起来将塑料熔化。螺杆将熔融塑料向前传动,直到它从挤出管道最后面一个洞中被挤出。• The extruder screw has several important functions to perform such as(1)conveyingtheresinthroughtheextruder,(2)imparting mechanicalenergyaspartofthemeltingprocess,(3)mixing ingredients together,(4)building pressure in the extruder so that the resin will be pushed through the die.One majordevelopment in screw design is the creation of twin-screw extruders, in which two screwsoperatetogethertoachieveuniqueperformance characteristics.挤出机螺杆有几个重要的功能要执行，比如(1)输送树脂通过挤出机、(2)提供熔化过程能量的一部分-机械能,(3)将配料混合在一起,(4)在挤出机中制造压力,以便推动树脂通过模具。在螺杆设计上一个主要的发展是创造双螺杆挤出机,两个螺杆一起运作实现独特的性能特征。

• In contrast to the extrusion process, which makes continuous parts of constant cross section, injection molding makes discrete parts that can have complex and variable cross sections as well as a range of surface textures and characteristics.The wide variety in the types of parts that can be made by injection molding is a key reason that more injection molding machines are used for plastics processing than any other type of molding equipment.Almost all thermoplastics and some thermosets can be injection molded, thus adding to the flexibility of the process.与能形成连续零件和稳定截面的挤出成型相比,注塑成型使独立的零件,可以有复杂多变的截面以及一系列的表面纹理和特点。通过注射成型可以制造各种各样的类型的零件，是注塑机器比任何其他类型的成型设备更多的用于塑料加工一个关键的原因。几乎所有的热塑性塑料、一部分热固性塑料可以通过注塑成型,这样就使加工的灵活性大大增加。

• Anotherimportantreasonforthepopularityofinjection molding is that parts are highly repeatable;that is, the parts can be made with very little part-to-part variation.Furthermore, injection molding is highly automatable with little postmolding finishing required in most parts and high output rates, so labor costs can be only a small portion of the part cost.注射成型大受欢迎的另一个重要的原因是,加工的零件是高度可重复的;也就是说,制造的零件零件间的变差可以很小。此外,注射成型是高度可自动化的，只需要很少的大部分零件所需的后成型加工，并且有很高的产出率,所以劳动力成本可以可以只占零件成本的一小部分。

• In injection molding, a plastic is melted and then forced into the cavity of a closed mold, which gives shape to the plastic.After sufficient time for the plastic part to solidify(usually by cooling), the mold is opened and the part is removed.在注塑成型中，塑料被融化,然后被强行注入使塑料成型的封闭的模具的型腔,。经过充分的时间使塑料零件凝固(通常通过冷却),模具打开和零件取出。

• 聚合物可以分为天然聚合物和合成聚合物。

The polymers can be further divided into natural polymers and synthetic polymers.• 大分子链的长度是决定大分子间相互作用的本质的关键因素。

The length of Macromolecular chain is the key factor to decide the intermolecular attraction between macromoleculars.• 常常称为通用塑料的树脂有聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯及这些基础树脂的各种改性产品。Some of the most commonplastics are polyethylene, polypropylene, polyvinyl chloride(PVC)and polystyrene and all kinds of modified products of these basic resin.• 材料吸收能量而不断裂的能力称为韧性。

The property ofMaterials that absord energy without fracture called toughness.• 蠕变是材料在静载荷下的逐渐变形。

The creep is that materials gradually deformation with static load.• 许多塑料材料的强度和模量能通过添加增强材料而获得提高。

Many plastic material can improve their strength and modulusby adding reinforcing materials.• 工程塑料通常具有高的强度、使用温度、良好的冲击强度和很宽温度范围内良好的尺寸稳定性。

Engineering plastics aregenerallystrongandhave,ahighuse temperature, good impact strength, good dimensional stability over awiderangeoftemperatures.• 聚合物的加工温度就是聚合物能方便的进行模塑成型的温度。

Polymer processing temperature is a certain temperature at which polymer can bemolding

conveniently.• 典型的塑料成型方法包括挤出模塑、注射模塑、压缩模塑、压延成型等。

The typical plastic molding methods includes extrusion molding, injection molding, compression molding, calendaring an so on..• 挤出生产线的主要部分包括挤出机、口模、冷却系统、牵引装置等。

Main part extrusion production lineincludes extrusion machine, die, cooling system, traction device, and so on.• 注射成型设备分为三个主要的功能段：注射单元、模具、合模系统。The injection molding equipment can be divided into three main function section: injection unit, mold, closing system.• 决定注射成型制件成本的主要因素包括材料种类、模具成本、模塑周期等。

The main factors of injection molding product cost includes material types, mould cost, molding cycle, etc.

第二篇：高分子加工助剂名词解释

1助剂是某些材料和产品在生产或加工过程中所需要添加的各种辅助化学品用以改善生产工艺和提高产品性能,树脂和生胶加工成塑料和橡胶制品这一过程中所需要的各种辅助化学品。

2喷聚:固体助剂的析出； 发汗:液体助剂的析出。

3焦烧现象：是指橡胶胶料在加工过程中产生的早期硫化的现象。

4促进剂的后效应：在硫化温度以下,不会引起早期硫化达到硫化温度时则硫化活性大的这种性质。5色母粒:是一种把超常量的颜料或染料均匀载附于树脂之中而制得的聚集体。

6增塑剂：是加进塑料体系中增加塑性同时又不影响聚合物本质特性的物质。

外增塑剂：一般为外加到聚合体系中的高沸点的较难挥发的液体或低熔点固体物质。

内增塑剂：在聚合物的聚合过程中引入能降低了聚合物分子链的结晶度增加了塑料的塑性第二单体物质。主增塑剂：分子既能插入聚合物的无定形区域同时又能插入结晶区域的增塑剂。

辅助增塑剂：分子仅能插入部分结晶的聚合物的无定形区域的增塑剂,此增塑剂又叫非溶剂型增塑剂。7相容性：增塑剂与树脂相互混合时的溶解能力,是增塑剂最基本要求之一。

8聚能密度(CED)：单位体积溶剂的蒸发能。9溶解度参数：单位体积溶剂的蒸发能的平方根所得值。1浊点(Tc)：聚合物与增塑剂的稀均相溶液,在冷却下变成浑浊时的温度。

2塑化效率：使树脂达到某一柔软程度的增塑剂用量称为该增塑剂的塑化效率。

3聚合物的氧化是指随着时间的增加聚合物的性能降低,又称为自动氧化。分为诱导期、强烈氧化期。4抗氧剂：是指对高聚物受氧化并出现老化现象能起到延缓作用的一类化学物质。

主抗氧剂：主抗氧剂被认为是一种自由基的清洗剂,它通过偶合反应(即终止反应)或给出一个氢原子来阻止聚合物中的自由基的破坏作用。辅助抗氧剂：助抗氧剂的作用是可分解聚合物氧化所产生的过氧化物。5金属离子钝化剂：具有防止重金属离子对聚合物产生引发氧化作用的物质。

6稳定剂：是防止或延缓聚合物在加工、贮藏和使用过程中老化变质的化学药品。

热稳定剂：主要用于PVC和其他含氯的聚合物,既不影响其加工与应用,又能在一定程度上起到延缓其热分解的作用的一类助剂。光稳定剂：凡能抑制或减缓光氧老化进行的的物质称为光稳定剂或紫外光稳定剂。7自由基捕获剂：是一类具有空间位阻效应的哌啶衍生物类光稳定剂,简称为受阻胺类光稳定剂(HALS)。8光氧老化或光老化：分子材料长期暴露在日光或短期置于强荧光下,由于吸收了紫外线能量,引起了自动氧化反应,导致了聚合物的降解,使得制品变色、发脆、性能下降,以致无法再用。

9阻燃剂：能够增加材料耐燃性的物质叫阻燃剂。0燃烧速度：指试样单位时间内燃烧的长度。1协同效应：指两种或两种以上的助剂配合使用时,其总效应大于单独使用时各个效应的总和。

协同作用体系：阻燃剂的复配是利用阻燃剂之间的相互作用,从而提高阻燃效能,称为协同作用体系。2燃烧速度：是指试样单位时间内燃烧的长度。燃烧速度是用水平燃烧法和垂直燃烧法等来测得。3氧指数：是指试样像蜡烛状持续燃烧时,在氮-氧混合气流中所必须的最低氧含量。

4外摩擦：高分子材料在成型加工时,聚合物熔体与加工设备表面间的摩擦。内摩擦：高分子材料在成型加工时,熔融聚合物分子间存在的摩擦。5润滑剂：为减少高分子内摩擦和外摩擦,改进塑料熔体的流动性,防止高分子材料在加工过程中对设备的粘附现象,保证制品表面光洁度而加入的物质称为润滑剂。6脱模剂：对加工模具和被加工材料完全保持化学惰性的物质称为脱模剂。

7发泡剂：是一类能使处于一定粘度范围内的液态或塑性状态的橡胶、塑料形成微孔结构的物质。

发泡助剂：发泡过程中,能与发泡剂并用并能调节发泡剂分解温度和分解速度的物质,或能改进发泡工艺,稳定泡沫结构和提高发泡体质量的物质。物理发泡剂:依靠在发泡过程中本身物理状态变化来达到发泡目地的一类化合物；化学发泡剂:在一定温度下会热分解而产生一种或多种气体,使聚合物发泡。

8抗静电剂：添加在树脂、燃料中或涂附在塑料制品、合成纤维表面的用以防止高分子材料和液体燃料静电危害的一类化学添加剂统称为抗静电剂。外用抗静电剂：采用涂布、喷雾、浸渍等方法使它附在塑料、纤维表面,耐久性较差,所以又叫做暂时性抗静电剂。内用型抗静电剂(或混炼型抗静电剂)：在树脂加工过程中(或在单体聚合过程中)添加到树脂组成中的抗静电剂,因其有较好的耐久性,又称为永久性抗静电剂。9偶联剂：是能改善填料与高分子材料之间界面特性的一类物质。

0着色剂：在聚合物中加入的改变制品颜色,提高制品美观性的助剂。

着色力：指颜料影响整个混合物料颜色的能力,着色力大,使用着色剂量就小,成本也低。

1遮盖力：指着色剂阻止光线穿透着色制品的能力。2增透剂：能改善结晶聚合物透明性的助剂。3迁移性：指着色剂向介质渗色或向接触的物质迁移的现象。一般地说,有机酸的无机盐(色淀性颜料)迁移性比较小；分子量较高者比较低者迁移性小。4防霉剂:(生物抑制剂)有抑制霉菌生长和杀灭霉菌的功能。5荧光增白剂：能增加塑料制品的白度、亮度使色彩更加鲜艳夺目的物质。

6防雾剂：又称流滴剂,是防止透明材料雾害的一类添加剂。

7老化：高分子材料在成型、贮存、使用过程中发生结构变化,逐渐地失去使用价值的现象。

第三篇：高分子材料加工工程专业

高分子材料加工工程专业

专业简介

学科：工学

门类：材料类

专业名称：高分子材料加工工程专业

高分子材料加工工程专业是1953年由中国科学院院士徐僖教授主持创建的，是原轻工部教学指导委员会主任单位和教材编写委员会主任委员单位，在全国居领先地位，是国内名牌专业。

专业信息

培养目标：本专业以培养面向世界、面向未来，具有国际竞争能力、创新能力、创业能力、管理能力的高分子材料加工工程专门人才为目标。

主要课程：高分子材料加工机械、机械设计、高分子材料与应用、塑机控制技术、塑料制品设计、塑机与模具制造、模具工程设计、塑料成型工艺学、金属材料及热处理、化工原理、高分子物理及化学、模具CAD/CAE、材料力学等。本专业通过工程制图、机械零件设计、塑料模具设计、塑料加工工程实验和模具CAD/CAE运用等实践环节训练，使学生除了掌握必要的专业基础知识和技能外，还具有熟练的工程技术应用技能。毕业生能从事塑料制品的成型原理、成型工艺、配方设计、产品与模具设计、成型机械设计、新型高分子结构材料及功能材料的理论研究、技术开发应用、生产管理以及教学工作。修业年限：4年。

授予学位：工学学士学位。

专业就业状况

轻工、化工、建材、电子电器、通讯、机械、交通、医疗和航天航空等大中型企业、科研院所和大专院校，以及石化、合成树脂企业。

院校分布部分

四川大学。

第四篇：制药专业外语考试（范文）

学号：姓名：班级：

1)Copy and Translate of Words and Expressions:

1.Pharmaceutical;2.enzyme;3.precursor;4.clinical;5.pharmacokinetics;6.subacute;7.impurity;

8.inhaler;9.capsule;10.foetal;11.preclinical;12.side effect;13.excretion;14.safely evaluation;15.highlight;16.optimum;17.isolation;18.hydroxyl group;19.base;20.acid;21.reflux;22.derivative;23.insoluble;24.acetone;25.chloroform;26.beaker;27.carboxyl group;28.insulin;29.disulfide;30.bond;

31.dimmer;32.monomer;33.gene;34.condense;35.zinc;36.solidstate;37.recombination;38.clone;39.bacterial;40.analog;41.diluent;42.binder;43.adhesive;44.mass;45.screening;46.mill;47.mix;48.dry;

49.formulation;50 nutrient;antiulcer;

2)Give an explanation of drug.3)List several administration ways of drug and translate.4)List several reasons for the termination of development of NCE’s(candidates)and translate.5)Translate the sentence into Chinese: The critical path for development of a new drug generally run

through the initial synthesis of compound, subacute toxicity studies and then the clinical program.6)List several key words for two types of safety test Page 58 para 4.and translate

7)Page 56 Part 4 Line 3: List several common dosage forms and translate.8)How to describe the isolation procedure?(isolation of caffeine from tea)

9)List two approaches to the synthesis of insulin and translate

10)List several disadvantages or limitations of liquid oral forms(just key words)when compared to the

tablets.11)List three options to introduction chirality into a synthesis and translation:

12)Translate：The goal of the Pharmaceutical Engineering Program is to train graduate students who are

proficient in using the modern tools of engineering analysis, built on a strong background in the mathematical, physical, chemical and biological sciences, for the design of pharmaceutical processes.Graduates will know how to apply engineering principles to interdisciplinary applications and work effectively in teams with other engineers and/or scientists.Our graduates will also know that it is important to engage in life-long learning in order to adapt to the constantly changing nature of cutting-edge technology.To this end, we teach students how to do critical, as well as thorough, objective-driven design exercises.Graduates are expected to be proficient in oral and written communication skills, to be team players and leaders.Graduates will have a good understanding of contemporary culture and issues necessary for good citizenship in our society and in the world.13)Try to write the cooresponding English abstract fluently.(2 topics for every student)

第五篇：高分子专业简介

包装工程专业

包装是产品的有机组成部分，存在于产品的生产、流通到消费领域的各个行业和环节，它不仅使产品美化、保质和升值，也是社会文明与进步的标志。包装涉及材料、力学、机械与美学等多种领域，是一个交叉性学科。包装工程专业依托我校高分子优势学科于2000年设立，以天然和合成有机高分子材料在包装上的应用与工程为主要特色，教学团队结构合理，实验仪器设备齐全。

印刷工程专业

我校的印刷工程专业是在我校高分子材料学科的基础上衍生发展起来的一门综合性应用学科。专业建设遵循教育部印刷专业本科教育指导委员会所制定的教学方针，以融汇高分子材料科学、包装工程、计算机技术、光学与美学等相关学科专业的知识与技术为特色，逐步形成了印刷材料与印刷工程的教学和科研体系，合理的教学团队和完备的实验仪器设备保证了高质量人才的培养。

高分子材料与工程（包括橡胶工程、塑料工程、高分子合成三个专业方向）

高分子材料与工程涉及高分子量有机化合物的设计合成、结构性能、化学与物理改性、成型加工及其应用，是当代材料科学与工程的重要组成部分。本校高分子材料与工程专业发端于1950年设立的橡胶工艺专业，经60年的积累和发展，已成为青岛科技大学的传统和特色学科，也是山东省重点建设的优势学科，2008年又被评为国家级特色专业。依托该学科建立有橡塑材料与工程教育部重点实验室、高性能聚合物及成型技术教育部工程研究中心和国家轮胎工艺与控制工程技术研究中心。目前，本学科已发展成为我国橡胶与塑料加工工程和高分子材料合成的重要科研与开发基地，在高分子基础材料和先进材料的人才培养方面独具特色，我国高分子工业，特别是橡胶企业的领军人物和工程技术骨干大都出自我校高分子学科及其相关专业。